Design, synthesis, and performance evaluation of TiO2

Scientific Reports volume 13, Article number: 13825 (2023) Cite this article

129 Accesses

1 Altmetric

Metrics details

We report on the synthesis and characterization of six novel 2,2′-bithiophene-based organic compounds (3a–c and 5a–c) that are designed to serve as co-sensitizers for dye-sensitized solar cells (DSSCs) based on TiO2. The compounds are linked to various donor and acceptor groups, and we confirm their chemical structures through spectral analyses. Our focus is on enhancing the performance of metal based N3, and the compounds were designed to operate at the nanoscale. We performed absorption and fluorescence emission measurements in dimethylformamide (DMF), where one of our compounds 5a exhibited the longest maximum absorption and maximum emission wavelengths, indicating the significant impact of the para methoxy group as a strong electron-donating group. Our dyes 5a + N3 (η = 7.42%) and 5c + N3 (η = 6.57%) outperformed N3 (η = 6.16%) alone, where the values of short current density (JSC) and open circuit voltage (VOC) for these two systems also improved. We also investigated the charge transfer resistance at the TiO2/dye/electrolyte interface using electrochemical impedance spectroscopy (EIS), which is important in the context of nanotechnology. According to the Nyquist plot, the 5a + N3 cocktail exhibited the lowest recombination rate, resulting in the highest VOC. Our theoretical calculations based on density functional theory (DFT) are also in agreement with the experimental process. These findings suggest that our compounds have great potential as efficient DSSC co-sensitizers. This study provides valuable insights into the design and synthesis of new organic compounds for use as co-sensitizers in DSSCs based on TiO2 and highlights the potential of these compounds for use in efficient solar energy conversion.

Solar cells manufactured using organic dyes, which are known as dye-sensitized solar cells (DSSCs), are a technology that falls under future technologies for the manufacture of solar cells at a low cost1,2,3,4. One of the essential principles in creating a dye-sensitized solar cell involves the creation of a highly porous nanocrystalline TiO2 layer5. This layer serves as the surface on which a photosensitizer, or dye, with a high molar extinction coefficient is chemically attached to form the working electrode of the solar cell. The working electrode is then separated from a platinum counter-electrode by an iodide-triiodide liquid electrolyte6,7. The electrolyte contains a redox couple, as \(I_{3}^{ - } / I^{ - }\), closed by a counter electrode (often platinum)8.

Photosensitizers are a crucial component of DSSCs as they have the ability to convert incident light into excited electrons that can be used to generate electrical current. This makes their role critical in the overall performance of the DSSC, compared to other components9. There are two types of dyes that have shown efficiency when used in this application. The first type, which is a metal-free organic dye, is characterized by its high absorption strength and depends on the use of donor moieties such as phenothiazine, indoline, carbazole, triphenylamine and natural dye such as Betalain and Anthocyanin, extracted from beetroot and cranberries, or a blend of three natural photosensitizers derived from Roselle, spinach, and beetroot10, to improve the efficiency of DSSCs11,12,13, linker to the acceptor moieties diketopyrrolopyrrole, benzothiadiazole, cyanoacetamides, and benzotriazole14,15,16,17,18. The second type is metal-based dyes, the most famous of which are ruthenium compounds such as cis-Bis(isothiocyanato) bis(2,2′-bipyridyl-4,4′-dicarboxylato ruthenium(II) N3, di-tetrabutylammonium cis-bis(isothiocyanato)bis(2,2′-bipyridyl-4,4′-dicarboxylato)ruthenium(II) N719, and black dye19,20. The performance of the second type is better than the first, but it is disadvantaged by its high cost and complex preparation methods21,22,23. In order to take advantage of both types, the co-sensitization process, which is the use of different types of p; dyes in the same preparation, was used in this application24,25,26,27,28.

Our research contributes to the growing body of knowledge on the development of efficient and low-cost DSSCs, which have significant implications for renewable energy. The use of organic compounds as co-sensitizers in DSSCs is an active area of research, and our findings have the potential to advance this field further. Overall, our research highlights the importance of developing innovative approaches to improve the performance of DSSCs, ultimately contributing to the global effort to transition towards sustainable and clean energy sources. Therefore, based on what has been mentioned, organic compounds (3a–c and 5a–c) that are easy to prepare and small in size have been prepared to be used as co-sensitizers to improve the commercial dye N3. The chemical composition of the different dyes and the commercial dye N3 is shown in Fig. 1.

Molecular structures of co-sensitizers 3a–c, 5a–c and N319.

The synthetic procedures for compounds 3a–c and 5a–c are provided in the supplementary file. The bithienylbenzonitrile derivatives 3a–c were prepared via refluxing bromo bithienyl derivative 129 with 4-methoxyphenylboronic acid (2a), 3,4-dimethoxyphenylboronic acid (2b), and 3,5-dimethoxyphenylboronic acid (2c) in 1,4-dioxane as a solvent using Pd(PPh3)4 as a catalyst, and K2CO3 as a base (Fig. 2). Compound 3a is prepared with updated procedure by Suzuki coupling reaction with good yield (75%) compared to 51% of the previous work30.

Synthesis scheme for the bithienylbenzonitrile derivatives.

The elemental and spectral analyses were used to confirm the structures of bithienylbenzonitrile derivatives 3a-c. The corresponding figures (Figures 1–9) are provided in the supplementary files. 1H-NMR spectrum of compound 3b displayed two singlet signals of dimethoxy groups at δ 3.78 (para -OCH3), 3.83 (meta OCH3), two doublet signals, at δ 6.99 (J = 8.5 Hz), δ 7.22 (J = 2.5 Hz), along with doublet of doublet signal at δ 7.20 (J = 8.5, 2.5 Hz) corresponding for 1,3,4-trisubstituted benzene ring, and four signals as doublet referring to bithiophene-H’s at δ 7.40 (1H), 7.41 (1H), 7.46 (1H), and 7.74 (1H). In addition to, singlet signal at δ 7.86 (4H) of benzonitrile-H’s. Mass spectrum of compound 3b gave a molecular ion peak m/z at 403 (M+, 100), along with a fragment at 388 (M+-CH3).

Figure 3 outlines the preparation of the bithienylfluorobenzonitrile derivatives 5a–c starting with a Suzuki coupling reaction via cross-coupling reaction of bromo bithienyl derivative 431 with the proper phenylboronic acids 2a–c. Structures of bithienylfluorobenzonitriles 5a–c were confirmed based on their elemental and spectral analyses. The corresponding figures (Figures 10–18) are provided in the supplementary files. IR spectra of the bithienyl fluorobenzonitriles 5a-c indicated the presence of cyano group with stretching vibrations in the range of 2228–2229 cm−1. 1H-NMR spectrum of bithienyl flurobenzonitrile derivative 5a displayed singlet signal referring to para -OCH3 at δ 3.78, AA’BB’ splitting pattern of two doublet signals at δ 6.98, 7.61 (J = 8.5 Hz, two protons each) of Ar–H of 4-methoxyphenyl ring and two doublet signals one proton each (J = 3.5 Hz) of one thiophene moiety and multiplet signal referring to 2H of the other thiophene moiety, along with doublet of doublet at δ 7.67 (J = 8.0, 1.5 Hz) and multiplet signal corresponding for 1,3,4-trisubstituted benzene ring. Moreover, mass spectrum of compound 5a gave a molecular ion peak m/z at 391 (M+, 100) as a base peak, along with a fragment at 376 (M+-CH3) as outlined in Fig. 4.

Synthesis scheme for the bithienylfluorobenzonitrile derivatives 5a–c.

Mass fragmentation patterns of bithienylfluorobenzonitriles 5a, 5b.

1H-NMR spectrum of compound 5b showed two singlet signals referring to 3,4-dimethoxy groups at δ 3.78 (para -OCH3), 3.83 (meta -OCH3), two doublet signals, at δ 6.99 (J = 8.0 Hz), δ 7.25 (J = 1.5 Hz), along with doublet of doublet at δ 7.22 (J = 8.0, 1.5 Hz) corresponding for 1,3,4-trisubstituted benzene ring, and four signals referring to bithiophene-H’s; in addition to, two signals integrated for Ar–H’s of fluorobenzonitrile ring. Mass spectrum of compound 5b gave a molecular ion peak m/z at 421 (M+, 100) as a base peak, along with a fragment at 406 (M+-CH3) due to loss of a methyl group, mass fragmentation patterns (Fig. 4) were in consistent with the reported literature32.

The absorption and fluorescence emission measurements were performed in DMF. The bathochromic shift observed in the fluorescence emission spectra is not as pronounced as that observed in the corresponding absorption spectra. The wavelength of maximum absorption and E0–0 transition of the fluorescence emission spectra are collected in Table 1.

As shown in Figure 19 in supplementary file presents a simple class of D–π–A that clearly shows the structural influence of the electron donor and electron acceptor groups. Bithiophene derivative 5a shows the maximum absorbance \({\uplambda }_{{{\text{max}}}}^{{{\text{abs}}}}\) and maximum a emission \({\uplambda }_{{{\text{max}}}}^{{{\text{em}}}}\) indicating the effect of methoxy group as strong electron donating group and enhanced strength of the electron withdrawing cyano group by the presence of fluorine atom in its ortho position. Bithiophene derivatives 3c and 5c are similar in the electron donating meta-dimethoxy groups which approximately shows same fluorescence emission maximum and few nanometres bathochromic shift with the fluorinated analogue. The fluorinated analogue of the ortho-dimethoxy derivatives were found to enhance the bathochromic shift as has been observed for the para-mono methoxy analogue. This can be attributed to the presence of ICT process from the meta methoxy in the electron donating moiety to the meta fluorine atom in the acceptor group which interfere with the ICT from ortho methoxy to the cyano pathway. The absorption spectrum of N3 is displayed at Figure 20 in the supplementary file.

We also studied the UV–Vis spectrum of the dyes on the surface of the TiO2 (Fig. 5). Through the results, it became clear that the spectrum is broader than that of the solution. This confirms the absorption of the dyes on the surface of the TiO2. It was also observed that the dyes 5a–c had an absorption at a longer wavelength than that in the solution, which resulted from the J-aggregation33. The presence of two linkage groups (CN and F) results in the highest absorption of dyes 5a–c, whereas the cyano group is present alone in dyes 3a–c. The aforementioned results indicate that dyes 5a–c could give interesting results when used in DSSCs. The absorption spectrum of N3 anchored to TiO2 is displayed at Figure 21 in the supplementary file.

UV/Vis absorption of bithiophene dyes 3a–c and 5a–c absorbed over TiO2.

Figure 6 provides additional insight into the mechanism by which our nitrile dyes are anchored to the TiO2 surface. This anchoring process is supported by the fact that various compounds, including transition metal cyanides, have been observed to form visible charge-transfer (CT) complexes with Ti(IV) ions on surfaces34,35,36. This results in strong dye-to-TiO2 charge-transfer (DTCT) bands, indicating that the nitrile group-containing compounds, (3a–c and 5a–c), serve as effective anchoring groups for TiO2.

Molecular structure of 5a binding to the titania surface.

The nitrile dyes can undergo one-step electron injection to the conduction band (CB) of TiO2 in a DSSC, similar to transition metal cyanides. Therefore, developing dye systems for electron injection to TiO2 through this pathway is of great interest academically and practically36,37,38,39,40. In this study, we focused on sensitizers with nitrile units that bind to the surface of TiO2 through chelation of surface Ti(IV) ions41. Among the nitrile sensitizers, sensitizer 5a, which contains an electron-withdrawing group (F) and an electron-donating methoxy group, is the best model. The dipolar structure of 5a provides directionality to electronic orbitals in the excited state, which improves direct, "one-step" electron injection from the ground state of the dye to the CB of TiO2 via photoinduced charge-transfer excitation of the dye-to-TiO2 bands42. The acidic hydrogen relocates to the titanium complex during the shift to the titanium complex from the dyes Figure 22 in the supplementary file. The orbital distribution and energy levels of each dye following the interaction with the TiO2 surface were investigated to study the electronic connection between the LUMO of the dye and the conduction band CB of the semiconductor.

There are some requirements that must be met in order to use organic dyes in the field of DSSCs, which depend on the values of the ground state oxidation potential (GSOP) and excited state oxidation potential (ESOP)34. With the help of both the cyclic voltammetry and the UV–Vis spectrometer measurements, these values were calculated by the following equation43:

From Fig. 7, It was found that the ESOP values of the bithiophene dyes 3a–c and 5a–c are categorical (− 3.34 eV, − 3.41 eV, − 3.36 eV, − 2.72 eV, − 2.75 eV, and − 2.74 eV) in order. Since it is higher than the value of the conduction band of the TiO2 (− 4.2 eV), the electrons will automatically flow easily to the TiO235. On the other hand, the GSOP values for dyes were found as follows: − 6.10 eV (3a), − 6.13 eV (3b), − 6.20 eV (3c), − 5.37 eV (5a), − 5.63 eV (5b), and − 5.54 eV (5c). It was found at a lower level than the electrolyte (− 5.2 eV), which helps return electrons to the dye to start over44,45,46. All this means that the dyes met the conditions for their use in DSSCs. The 5a–c dyes achieved LUMO values at higher levels than the 3a–c dyes, which means that the flow rate of electrons in these dyes to the surface of the semiconductor is higher, and this also indicates that the dyes will give high efficiency when used in DSSCs.

Energy-level diagram of bithiophene dyes 3a–c and 5a–c.

Theoretical calculations using the density functional theory (DFT) of the Gaussian program were applied to delve deeper into the structural composition of the compounds under study. B3LYP/6-311G (d, p) was used as the functional model and basis set for the first optimization of the structures47,48,49. The values of GSOP, ESOP, E0–0, and simulated frontier molecular orbitals (FMOs) are displayed and calculated for the different affirmations, and they proved to be in agreement with the practical values that we obtained (Table 2).

Figure 8 shows the optimized structures, FMOS and MEP, of co-sensitizers 3a–c. From their FMOS, the distribution of the electrons in the HOMO is concentrated on the whole molecule, whereas in the LUMO, there was a shift to the acceptor part toward the cyano-moiety. The computed contributions of various electronic transitions, presented in Table 1 (supplementary file), suggest that the ICT in co-sensitizers 3a-c and 5a-c is characterized by a peak absorption in the 470–478 nm range, related to the large contribution of HOMO to LUMO transitions Meanwhile, the π–π* electronic transitions of the compounds, due to significant contributions of HOMO-n to LUMO + n transitions50. Using the same basis set and functional energy, we calculated the electrostatic potentials (MEPs) of the dyes under investigation. The MEP concentrates on anticipating physicochemical features like the reactive groups associated with the molecular structure51. Also, MEP is a graph of the electrostatic potential, plotted onto the constant electron density surface52. Different colors are used to show ESP levels. An electron-rich field is shown by the red area, while electron-poor sections are indicated by the blue region53.

The optimized structures, FMOS and MEP, of co-sensitizers 3a–c.

Also, Fig. 9 shows the optimized structures, FMOS and MEP, of co-sensitizers 5a–c. For co-sensitizers 5a–c, the distribution of the electrons in the HOMO is concentrated on the donor part, whereas in the LUMO, there was a shift to the acceptor part toward the acceptor-anchoring moiety, which indicated better charge transfer as shown in their FMO levels. MEP also demonstrated the high electron density parts and low charge parts according to their different colors, from red to blue.

The optimized structures, FMOS and MEP, of co-sensitizers 5a–b.

With an iodolyte electrolyte and simulated AM 1.5 G illumination, photocurrent density–voltage (I–V) curves of DSCs based on dyes 3a–b and 5a–b together with N3 were done. The supplementary file contains information on the fabrication process and instruments used for the photovoltaic measurements54,55,56. Because of what the previous measurements showed and the small size of the dyes 3a–c and 5a–c that were made, they were used as co-sensitizers in DSSCs to make the standard dye (N3) work better. Figure 10 displays the I–V curves of the co-sensitizers 3a–c, 5a–c and N3. The corresponding data is recorded in Table 3.

I-V characteristics curves of co-sensitizers 3a–b, and 5a–c with N3.

As shown in Table 3, dyes 5a + N3 (η = 7.42%) and 5c + N3 (η = 6.57%) achieved higher efficiencies than N3 (η = 6.16%) alone. The value of JSC and VOC for these two systems also improved. The dye absorbs the main dye, increasing the number of electrons flowing into the conductor and resulting in a high JSC value. As for the increase in VOC, it is due to the filling of the existing interstitial spaces due to the adsorption of the dyes, which led to a larger number of dyes that bore on the surface of the conductor, and this leads to a decrease in aggregation and an increase in the voltage. Also, the co-sensitization impact of 3a–c, 5a–c, and N3 was further investigated by measuring the loading onto the photoanode, which directly proportional to the photocurrent value. Table 3 summarizes the findings of measuring the concentration of co-sensitizers 3a–c, 5a–c, and N3 adsorbed on TiO2 using 0.1 M NaOH in a dimethylformamide and water (1:1) combination. As a result of its improved JSC and suitably expanded light collecting capacities, 5a provided the optimum co-sensitization performance. The increase in VOC and JSC consequently led to an increase in cell efficiency.

It is also noted that the dyes 3a–c did not achieve a positive effect on the dye N3, and this was originally due to the nature of the co-sensitizer and its inability to adhere well to the surface of the TiO2, i.e., an aggregation of the dye occurred, and the recombination increased, so the voltage decreased. Also, the N3 didn't get well absorbed because the N3 and co-sensitizer were aggregated together. This made it harder for electrons to get into the TiO2, so the JSC went down. Table 2 (Supplementary file) compares the performance parameters of 3a–c, 5a–c and N3 with recently reported high-performance sensitizer and co-sensitizer. Furthermore, the electronic distribution for co-sensitizers 3a–c, from Fig. 8, the HOMO for co-sensitizers 3a–c is randomly distributed throughout the framework, whereas the LUMOs were located in the anchoring parts (cyano units) through the biphenyl-spacer, this means that the LUMO electron destination does not really tightly coincide with TiO2’s conduction band (CB), which could lead to poor electron injection efficiency from the dyes' LUMO and so the JSC values went down comparing to the others co-sensitizers and increasing the charge recombination rate at the interface of the TiO2/dye/electrolyte, which can be related to the energy level alignment at the interface. The bithienyl co-sensitizers 5a–c exhibit efficient charge transfer between their highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) levels, as seen in Fig. 9. The electron density is primarily localized on the substituent anchoring groups, allowing for electronic interactions between the TiO2 d-orbitals and the LUMO electron density. Additionally, the coexistence of the HOMO and LUMO levels facilitates rapid photo-induced electron transfer from the donating portion to the acceptor group. Because of this increased charge separation, 5a has a much higher photovoltaic efficiency than other sensitizers. Further dye 5b did not improve the performance of the N3 although the increased in the JSC, which may be attributed to the recombination of the dye on the surface that result in the decreased VOC value and hence the decrease of the efficiency. To learn more about the mechanism of the absorption of dyes 3a–c and 5a–c on the surface of TiO2, the IR-spectrum of the dyes on the surface of TiO2 was measured, as shown in Figures 23–28 in the supplementary files. It was found that the value of the cyano group (CN) disappeared, or its absorption decreased in the samples, which confirms that the binding was through the cyano group. Figure 11 shows the incident photon-to-current conversion efficiency (IPCE) spectra of devices sensitized with N3 and co-sensitized with 2,2′-bithiophene-based 3a–c and 5a–c. The IPCE spectra for all these cells exhibited a broad response within a large wavelength range (300–650 nm), indicating that all the dyes can efficiently convert the visible light into photocurrent. The higher IPCE values of the devices co-sensitized with the bithiophene co-sensitizers 3a–c and 5a–c can be attributed to their improved photovoltaic characteristics. Additionally, N3-based cells fabricated with co-sensitizer 5a–c demonstrated higher quantum efficiency (IPCE value) than N719 alone, possibly due to the appropriate mixing of organic dye and Ru-II complex and presence of auxiliary electron withdrawing group. Furthermore, the increased IPCE values can be attributed to increased JSC values, the IPCE integral areas of DSSCs exhibit an order for dyes of 5a + N3 > 5c + N3 > 5b + N3 > N3 > 3a + N3 > 3b + N3 > 3c + N3, trend of is consistent with the trend of JSC. The cell co-sensitized by 5a + N3 had the highest IPCE response corresponding to its highest Jsc value of 18.14 mA cm−2 and gave over 65% IPCE values from 300 to 650 nm. This observation strongly advocates that during the dye loading process of co-sensitizers along with N3 should have interacted with each other. Such interaction generally tends to induce electron and energy transfer between the two kinds and hence causes deterioration in cell performance. The co-sensitized cell exhibits the highest Jsc value in the J-V measurements, which can be attributed to its broadest and highest IPCE response57. Additionally, the co-sensitized cell's improved Voc value, coupled with its highest Jsc value, contributes to its further increased PCE value when compared to that of 5a + N3, the improved IPCE response of (3a-c, and 5a-c is interpreted in terms of higher JSC value which showed the same order of 5a + N3 = 18.23 > 5c + N3 = 17.52 > 5b + N3 = 17.21 > 3a + N3 = 15.83 > 3b + N3 = 15.59 > 3c + N3 = 15.02 mA cm−2 compared to N3 (16.93 mA cm−2). These results implies that the structural optimization with 3a–c and 5a–c architecture is a key in getting greater efficiency, compared to the Jsc values obtained from the J–V data, the JscIPCE values integrated from the IPCE spectra are quite consistent. As a result, the co-sensitizer 5a dye produces the most abundant IPCE spectrum, proving that it also has the greatest Jsc. The enhanced IPCE replies match the enhanced Jsc results.

IPCE spectra and integrated currents of DSSCs based on co-sensitizers 3a–b, and 5a–c with N3.

On the other hand, the value of cyano and F disappeared for 5a–c, which confirms the association of these dyes with cyano and fluorine together. Electrochemical impedance spectroscopy (EIS) was used to study the charge transfer resistance at the TiO2/dye/electrolyte interface58,59. This was done to learn more about the relationship between the structure of the molecules and their photovoltaic performance. The middle area shown in the Nyquist plot, as shown in Fig. 12, represents the relationship between the TiO2, the dye, and the electrolyte. The diameter of this part of the curve has a clear relationship with dye recombination; the larger the diameter, the less likely it is to be recombined, resulting in an increase in open circuit voltage60. On the Nyquist plots, the radius of the large semicircle in the middle frequency range was found to be 5a + N3 > 5c + N3 > N3 > 5b + N3 > 3b + N3 > 3a + N3 > 3c + N3, which shows the order of charge recombination resistance Rrec at the TiO2/dye/electrolyte interface. DSSCs with an increasing Rrec value have slower charge recombination between the electron injected and \(I_{3}^{ - }\) ions in the electrolyte. The charge recombination resistance of these dyes (RCT) corresponding to the diameter of the middle frequency semicircle was calculated to decrease in the order of 5a + N3 (23.21 Ω), 5c + N3 (21.24 Ω), N3 (20.34 Ω), 5b + N3 (18.19 Ω), 3b + N3 (16.58 Ω), 3a + N3 (15.56 Ω), 3c + N3 (14.29 Ω), in good agreement with the order photovoltage data. As a result, the Voc increases. Accordingly, this sequence of Voc values appears to be consistent. As a result, the 5a + N3 system with the largest diameter has the lowest recombination rate and the highest VOC, which is consistent with the photovoltaic values.

Nyquist plots of compounds 3a–c and 5a–c with N3 based.

In Bode frequency plots Fig. 13, by applying the following equation the electron lifetime for injected electrons into TiO2 conduction band can be calculated by (τeff = 1/2πf)58, where τ represents the electron lifetime injected into TiO2 and f is the mid-frequency peak in bode plots, which is directly related to the electron lifetimes. The electron lifetimes of DSSCs that were sensitized using co-sensitizers were determined through Bode frequency plots. By analyzing the Bode phase plots, the frequency of the peaks observed in the middle-frequency domain can be used to assess the electron lifetime within the semiconductor (τr (ms). This provides additional insight into the charge recombination rate occurring at the interface of TiO2/dye/electrolyte. The values of the mid-frequency peaks of the bode plots displayed the order: 5a + N3 > 5c + N3 > N3 > 5b + N3 > 3b + N3 > 3a + N3 > 3c + N3, indicating the corresponding electron lifetimes ranked as: 5a + N3 (4.38 ms) > 5c + N3 (3.56 ms) > N3 (3.40 ms) > 5b + N3 (2.62 ms) > 3b + N3 (1.64 ms) > 3a + N3 (1.52 ms) > 3c + N3 (1.26 ms), also coincided well with Voc. The electron lifetime and charge recombination rate at the interface of TiO2/dye/electrolyte are affected by factors such as the size and shape of the dye molecule54, as well as the dye adsorption behavior. These factors have a strong influence on the photovoltage of solar cells, as has been previously reported in the literature. In this study, the values of Rrec and se for the new co-sensitizer dyes were found to be consistent with the corresponding VOC values obtained for the solar cells. The use of the 5a co-sensitizer in DSSCs resulted in higher VOC values compared to other sensitizers, including N3, due to the lower charge recombination rate at the TiO2/dye/electrolyte interface, which is attributed to the strength of the donating moiety.

EIS Bode plots of compounds 3a–c and 5a–c with N3 based.

The stability of dye-sensitized solar cells (DSSCs) is a key issue that must be addressed to ensure their long-term viability as a renewable energy technology, the stability of co-sensitizers has been measured and added into the manuscript, As depicted in Fig. 14, the high photo-stability of the 3a–c and 5a–c/N3 dyes for DSSC applications is confirmed by the fact that the cell exhibits excellent stability with no discernible degradation of the initial performances even after 100 h of illumination. The superior long-term stability of co-sensitizer 5a may be attributed to the hydrophobic properties of the substituted methoxy group attached to bithienyl spacer addition to acceptors moieties (F and CN).

Stability of 3a–c and 5a–c with N3 based.

Our team accomplished significant success by designing and synthesizing six organic dyes (3a–c and 5a–c) using a simple yet effective D–π–A structure. By displaying the structural effects of electron donor and acceptor groups, these dyes have evaluated a new trend for improving the photovoltaic capabilities of dye-sensitized solar cells (DSSCs). To evaluate the efficiency of our dyes, we co-sensitized them with the standard dye N3. The absorption spectra of co-sensitized TiO2 films become more intense and broader than the individual dyes. The EIS data indicates a reduced recombination of injected electrons with the triiodide ions and a longer electron lifetime. Therefore, an improvement of open circuit photovoltage (Voc) is achieved for 5a and 5c. Under optimal conditions, the power conversion efficiency ranges (4.13–7.42%) and short circuit current (JSC) range (14.13–18.14 mA cm−2). Our mixed dyes 5a and N3 exhibited a remarkable efficiency of 7.42%, and with further optimization, we obtained a short-circuit current density of 18.14 mA cm−2 and a high open-circuit voltage (VOC) of 0.676 V. The exceptional JSC value can be attributed to the presence of two linkage groups (CN and F) that increase the absorption of dye 5a, as confirmed by the UV–Vis absorption over TiO2 surfaces. The maximum VOC value, on the other hand, is due to the extensive surface area covered by both dyes 5a and N3. The increase in Jsc and Voc are strongly correlated to enhance light absorption and reduced charge recombination, respectively. Our findings suggest that tuning the electron-donating groups is critical to improving the light-harvesting efficiency of co-sensitizers.

All data supporting the conclusions of this article are included within the article and supplementary document.

Panwar, N. L., Kaushik, S. C. & Kothari, S. Role of renewable energy sources in environmental protection: A review. Renew. Sustain. Energy Rev. 15, 1513–1524 (2011).

Article Google Scholar

Grätzel, M. Photoelectrochemical cells. Nature 414, 338–344 (2001).

Article ADS PubMed Google Scholar

Arshad, M. et al. In silico modeling and exploration of new acceptor molecules with enhanced power conversion efficiency for high-performance organic solar cell applications. J. Solid State Chem. 323, 124018 (2023).

Article CAS Google Scholar

Zheng, P. et al. Novel dual acceptor (D–D′–A′–π–A) dye-sensitized solar cells based on the triarylamine structure and benzothiadiazole double electron withdrawing unit. New J. Chem. 45, 4443–4452 (2021).

Article CAS Google Scholar

Atilgan, A. & Yildiz, A. Ni-doped TiO2/TiO2 homojunction photoanodes for efficient dye-sensitized solar cells. Int. J. Energy Res. 46, 14558–14569 (2022).

Article CAS Google Scholar

Mehboob, M. Y., Hussain, R., Irshad, Z. & Adnan, M. Role of acceptor guests in tuning optoelectronic properties of benzothiadiazole core based non-fullerene acceptors for high-performance bulk-heterojunction organic solar cells. J. Mol. Model. 27, 1–16 (2021).

Article Google Scholar

Birel, Ö., Nadeem, S. & Duman, H. Porphyrin-based dye-sensitized solar cells (DSSCs): A review. J. Fluoresc. 27, 1075–1085 (2017).

Article CAS PubMed Google Scholar

Das, P. et al. Waste chimney oil to nanolights: A low cost chemosensor for tracer metal detection in practical field and its polymer composite for multidimensional activity. J. Photochem. Photobiol. B Biol. 180, 56–67 (2018).

Article CAS Google Scholar

Yildiz, A. et al. Efficient iron phosphide catalyst as a counter electrode in dye-sensitized solar cells. ACS Appl. Energy Mater. 4, 10618–10626 (2021).

Article CAS Google Scholar

Teja, A. S. et al. Optimal processing methodology for futuristic natural dye sensitized solar cells and novel applications. Dyes Pigm. 210, 110997 (2022).

Article Google Scholar

Singh, A. K. & Nithyanandhan, J. Indoline-based donor-π-acceptor visible-light responsive organic dyes for dye-sensitized solar cells: Co-sensitization with squaraine dye for panchromatic IPCE response. ACS Appl. Energy Mater. 5, 1858–1868 (2022).

Article CAS Google Scholar

Elmorsy, M. R., Badawy, S. A., Salem, K. E., Fadda, A. A. & Abdel-Latif, E. New photosensitizers that are based on carbazoles and have thiophene bridges with a low bandgap do 32% better than N719 metal complex dye. J. Photochem. Photobiol. A. 436, 114421 (2022).

Article Google Scholar

Elmorsy, M. R., Badawy, S. A., Abdel-Latif, E., Assiri, M. A. & Ali, T. E. Significant improvement of dye-sensitized solar cell performance using low-band-gap chromophores based on triphenylamine and carbazole as strong donors. Dyes Pigm. 214, 111206 (2023).

Article CAS Google Scholar

Souilah, M., Hachi, M., Fitri, A., Benjelloun, A. T., Benzakour, M., Mcharfi, M. & Zgou, H. Improved photovoltaic performances of coumarin derivatives by forming DA′-Π-A structure using diketopyrrolopyrrole as auxiliary acceptor. SSRN 4116061 (2022).

Gonzalez-Flores, C. A. et al. Influence of redox couple on the performance of ZnO dye solar cells and minimodules with benzothiadiazole-based photosensitizers. ACS Appl. Energy Mater. 5, 14092–14106 (2022).

Article CAS PubMed PubMed Central Google Scholar

Badawy, S. A., Abdel-Latif, E., Fadda, A. A. & Elmorsy, M. R. Synthesis of innovative triphenylamine-functionalized organic photosensitizers outperformed the benchmark dye N719 for high-efficiency dye-sensitized solar cells. Sci. Rep. 12, 1–17 (2022).

Article Google Scholar

Aldusi, A. M., Fadda, A. A., Ismail, M. A. & Elmorsy, M. R. Simple organic dyes containing multiple anchors as effective co-sensitizers for DSSCs loaded with Ru(II) complex N-719. Appl. Organomet. Chem. 36, 6893 (2022).

Article Google Scholar

Elmorsy, M. R. et al. New cyanoacetanilides based dyes as effective co-sensitizers for DSSCs sensitized with ruthenium(II) complex (HD-2). J. Mater. Sci. Mater. Electron. 31, 7981–7990 (2020).

Article CAS Google Scholar

Nazeeruddin, M. K. et al. Conversion of light to electricity by cis-X2bis (2, 2’-bipyridyl-4, 4′-dicarboxylate) ruthenium(II) charge-transfer sensitizers (X= Cl-, Br-, I-, CN-, and SCN-) on nanocrystalline titanium dioxide electrodes. J. Am. Chem. Soc. 115, 6382–6390 (1993).

Article CAS Google Scholar

Nazeeruddin, M. K. et al. Engineering of efficient panchromatic sensitizers for nanocrystalline TiO2-based solar cells. J. Am. Chem. Soc. 123, 1613–1624 (2001).

Article CAS PubMed Google Scholar

Ansari, M. I. H., Qurashi, A. & Nazeeruddin, M. K. Frontiers, opportunities, and challenges in perovskite solar cells: A critical review. J. Photochem. Photobiol. C Photochem. Rev. 35, 1–24 (2018).

Article CAS Google Scholar

Mathew, S. et al. Dye-sensitized solar cells with 13% efficiency achieved through the molecular engineering of porphyrin sensitizers. Nat. Chem. 6, 242–247 (2014).

Article CAS PubMed Google Scholar

Giribabu, L., Kanaparthi, R. K. & Velkannan, V. Molecular engineering of sensitizers for dye-sensitized solar cell applications. Chem. Rec. 12, 306–328 (2012).

Article CAS PubMed Google Scholar

Abdelhamed, F. H., Ismail, M. A., Abdel-Latif, E., Abdel-Shafi, A. A. & Elmorsy, M. R. Design and synthesis of novel bichalcophene derivatives with double anchoring groups for dye-sensitized solar cell applications: Sensitization and co-sensitization with N-719. J. Mater. Sci. Mater. Electron. 33, 15665–15678 (2022).

Article CAS Google Scholar

Kharkwal, D., Sharma, N., Gupta, S. K. & Negi, C. M. S. Enhanced performance of dye-sensitized solar cells by co-sensitization of metal-complex and organic dye. Sol. Energy 230, 1133–1140 (2021).

Article ADS CAS Google Scholar

Koteshwar, D. et al. Effects of methoxy group (s) on D–π–A porphyrin based DSSCs: Efficiency enhanced by co-sensitization. Mater. Chem. Front. 6, 580–592 (2022).

Article CAS Google Scholar

Alnakeeb, A., Fadda, A. A., Ismail, M. A. & Elmorsy, M. R. Efficient co-sensitization of novel trimethoxybenzene-based dyes with N-719 for highly efficient dye-sensitized solar cells. Opt. Mater. 128, 112344 (2022).

Article CAS Google Scholar

Devadiga, D. et al. The improved performance of dye-sensitized solar cells using co-sensitization and polymer gel electrolyte. Int. J. Energy Res. 46, 12974–12987 (2022).

Article CAS Google Scholar

Ismail, M. A. An efficient synthesis of 5’-(4-cyanophenyl)-2,2’-bifuran-5-carbonitrile and analogues. J. Chem. Res. 11, 733–737 (2006).

Article Google Scholar

Yokooji, A., Satoh, T., Miura, M. & Nomura, M. Synthesis of 5, 5′-diarylated 2,2′-bithiophenes via palladium-catalyzed arylation reactions. Tetrahedron 60, 6757–6763 (2004).

Article CAS Google Scholar

Ismail, M. A. et al. Novel cationic aryl bithiophene/terthiophene derivatives as corrosion inhibitors by chemical, electrochemical and surface investigations. Sci. Rep. 12, 3192 (2022).

Article ADS CAS PubMed PubMed Central Google Scholar

Ismail, M. A., Abdel-Rhman, M. H., Abdelwahab, G. A. & Hamama, W. S. Synthesis and spectroscopic studies of methoxysubstituted phenylthienylnicotinamidines. Synth. Commun. 50, 2355–2375 (2020).

Article CAS Google Scholar

Yang, J. et al. Influence of the donor size in D–π–A organic dyes for dye-sensitized solar cells. J. Am. Chem. Soc. 136, 5722–5730 (2014).

Article CAS PubMed Google Scholar

Blackbourn, R. L., Johnson, C. S. & Hupp, J. T. Surface intervalence enhanced Raman scattering from ferrocyanide on colloidal titanium dioxide. A mode-by-mode description of the Franck–Condon barrier to interfacial charge transfer. J. Am. Chem. Soc. 113, 1060 (1991).

Article CAS Google Scholar

Yang, M., Thompson, D. W. & Meyer, G. Charge-transfer studies of iron cyano compounds bound to nanocrystalline TiO2 surfaces. J. Inorg. Chem. 41, 1254 (2002).

Article CAS Google Scholar

Khoudiakov, M., Parise, A. R. & Brunschwig, B. S. Interfacial electron transfer in FeII(CN)64−–sensitized TiO2 nanoparticles: A study of direct charge injection by electroabsorption spectroscopy. J. Am. Chem. Soc. 125, 4637 (2003).

Article CAS PubMed Google Scholar

Lu, H., Prieskorn, J. N. & Hupp, J. T. Fast interfacial electron transfer: Evidence for inverted region kinetic behaviour. J. Am. Chem. Soc. 115, 4927 (1993).

Article CAS Google Scholar

Weng, Y.-X., Wang, Y.-Q., Asbury, J. B., Ghosh, H. N. & Lian, T. Back electron transfer from TiO2 nanoparticles to FeIII(CN)63−: Origin of non-single-exponential and particle size independent dynamics. J. Phys. Chem. B. 104, 93 (2000).

Article CAS Google Scholar

Ramakrishna, G. & Ghosh, H. N. Emission from the charge transfer state of xanthene dye-sensitized TiO2 nanoparticles: A new approach to determining back electron transfer rate and verifying the marcus inverted regime. J. Phys. Chem. B. 105, 7000 (2001).

Article CAS Google Scholar

Walters, K. A., Gaal, D. A. & Hupp, J. T. Interfacial charge transfer and colloidal semiconductor dye-sensitization: Mechanism assessment via Stark emission spectroscopy. J. Phys. Chem. B. 106, 5139 (2002).

Article CAS Google Scholar

Reddy, P. Y. et al. Angew. Chem. Int. Ed. 46, 373 (2007).

Article CAS Google Scholar

Basham, J. I., Mor, G. K. & Grimes, C. A. ACSNANO 4, 1253 (2010).

CAS Google Scholar

Luo, J. et al. Co-sensitization of dithiafulvenyl-phenothiazine based organic dyes with N719 for efficient dye-sensitized solar cells. Electrochim. Acta 211, 364–374 (2016).

Article CAS Google Scholar

Huang, Z.-S. et al. Dithienopyrrolobenzothiadiazole-based organic dyes for efficient dye-sensitized solar cells. J. Mater. Chem. A. 2, 15365–15376 (2014).

Article CAS Google Scholar

Tian, H. et al. Effect of different electron donating groups on the performance of dye-sensitized solar cells. Dyes Pigm. 84, 62–68 (2010).

Article CAS Google Scholar

Zhao, J., Yang, X., Cheng, M., Li, S. & Sun, L. Molecular design and performance of hydroxylpyridium sensitizers for dye-sensitized solar cells. ACS Appl. Mater. Interfaces 5, 5227–5231 (2013).

Article CAS PubMed Google Scholar

Frisch, M. J., Trucks, G. W., Schlegel, H. B., Scuseria, G. E., Robb, M. A., Cheeseman, J. R., Scalmani, G., Barone, V., Mennucci, B., Petersson, G. A., Nakatsuji, H., Caricato, M., Li, X., Hratchian, H. P., Izmaylov, A. F., Bloino, J., Zheng, G., Sonnenberg, J. L., Hada, M., Ehara, M., Toyota, K., Fukuda, R., Hasegawa, J., Ishida, M., Nakajima, T., Honda, Y., Kitao, O., Nakai, H., Vreven, T., Montgomery Jr., J. A., Peralta, J. E., Ogliaro, F., Bearpark, M., Heyd, J. J., Brothers, E., Kudin, K. N., Staroverov, V. N., Kobayashi, R., Normand, J., Raghavachari, K., Rendell, A., Burant, J. C., Iyengar, S. S., Tomasi, J., Cossi, M., Rega, N., Millam, J. M., Klene, M., Knox, J. E., Cross, J. B., Bakken, V., Adamo, C., Jaramillo, J., Gomperts, R., Stratmann, R. E., Yazyev, O., Austin, A. J., Cammi, R., Pomelli, C., Ochterski, J. W., Martin, R. L., Morokuma, K., Zakrzewski, V. G., Voth, G. A., Salvador, P., Dannenberg, J. J., Dapprich, S., Daniels, A. D., Farkas, O., Foresman, J. B., Ortiz, J. V., Cioslowski, J. & Fox, D. J. (Gaussian 09 Gaussian, Inc., 2010).

Nielsen, A. B. & Holder, A. J. Gauss View 5.0, User’s Reference (GAUSSIAN Inc., 2009)

Lee, C. T., Yang, W. T. & Parr, R. G. Development of the Colle–Salvetti correlation-energy formula into a functional of the electron density. Phys. Rev. B 37, 785 (1988).

Article ADS CAS Google Scholar

Arbelo-Lópezlópez, H. D. et al. Charge transfer and π to π* transitions in the visible spectra of sulfheme met isomeric structures. J. Phys. Chem. B 122, 4955 (2018).

Google Scholar

Murray, J. S. & Sen, K. Molecular Electrostatic Potentials: Concepts and Applications 1st edn, 664 (Elsevier, 1996).

Google Scholar

Shakila, G., Saleem, H. & Sundaraganesan, N. FT-IR, FT-Raman, NMR and U–V Spectral investigation: Computation of vibrational frequency, chemical shifts and electronic structure calculations of 1-bromo-4-nitrobenzene. World Sci. News 61, 150–185 (2017).

CAS Google Scholar

Raftani, M., Abram, T., Bennani, M. N. & Bouachrine, M. Theoretical study of new conjugated compounds with a low bandgap for bulk heterojunction solar cells: DFT and TD-DFT study. Results Chem. 2, 138277–138277 (2020).

Article Google Scholar

Neale, N. R., Kopidakis, N., De Lagemaat, J. V., Gratzel, M. & Frank, A. J. Effect of a coadsorbent on the performance of dye-sensitized TiO2 solar cells: shielding versus band-edge movement. J. Phys. Chem. B 109, 23183–23189 (2005).

Article CAS PubMed Google Scholar

Ito, S. et al. High-conversion-efficiency organic dye-sensitized solar cells with a novel indoline dye. Chem Commun. 41, 5194–5196 (2008).

Article Google Scholar

El-Shafei, A., Hussain, M., Atiq, A., Islam, A. & Han, L. A novel carbazole-based dye outperformed the benchmark dye N719 for high efficiency dye-sensitized solar cells (DSSCs). J. Mater. Chem. 22, 24048–24056 (2012).

Article CAS Google Scholar

Yan, R. et al. Ethynylene-linked planar rigid organic dyes based on indeno [1, 2-b] indole for efficient dye-sensitized solar cells. Dyes Pigm. 141, 93–102 (2017).

Article CAS Google Scholar

Oskam, G., Bergeron, B. V., Meyer, G. J. & Searson, P. C. Pseudohalogens for dye-sensitized TiO2 photoelectrochemical cells. J. Phys. Chem. B 105, 6867–6873 (2001).

Article CAS Google Scholar

Hua, Y. et al. Bulky dendritic triarylamine-based organic dyes for efficient co-adsorbent-free dye-sensitized solar cells. J. Power Sources 237, 195–203 (2013).

Article CAS Google Scholar

Qu, P. & Meyer, G. J. Proton-controlled electron injection from molecular excited states to the empty states in nanocrystalline TiO2. Langmuir 17, 6720–6728 (2001).

Article CAS Google Scholar

Download references

The authors are thankful to Mansoura University, Egypt, for their support under project ID: MU-SCI-22-31.

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Department of Chemistry, Faculty of Science, Mansoura University, El-Gomhoria Street, Mansoura, 35516, Egypt

Mohamed R. Elmorsy, Fatma H. Abdelhamed, Safa A. Badawy, Ehab Abdel-Latif & Mohamed A. Ismail

Department of Chemistry, Faculty of Science, Ain Shams University, Abbassia, Cairo, 11566, Egypt

Ayman A. Abdel-Shafi

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

M.R.E.: Conceptualization, formal analysis, investigation, writing-original draft. F.H.A. and S.A.B.: Data curation, formal analysis, methodology, and software; E.A.-L. and A.A.A.-S.: Investigation and writing—review and editing; M.A.I.: Supervision and Project administration.

Correspondence to Mohamed R. Elmorsy.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Elmorsy, M.R., Abdelhamed, F.H., Badawy, S.A. et al. Design, synthesis, and performance evaluation of TiO2-dye sensitized solar cells using 2,2′-bithiophene-based co-sensitizers. Sci Rep 13, 13825 (2023). https://doi.org/10.1038/s41598-023-40830-1

Download citation

Received: 09 June 2023

Accepted: 17 August 2023

Published: 24 August 2023

DOI: https://doi.org/10.1038/s41598-023-40830-1

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.